| Product Name | Product Size | Grades | Thickness | Finish |
|---|---|---|---|---|
| Stainless Steel Round Pipes | 1/2 Inch (12.7 mm) to 5 Inch (127mm) | JT, 304, 316, 316L | 26 Gauge (0.6mm) to 14 Gauge (2.0mm) | Mirror Finish & Matt Finish |
| Stainless Steel Square Pipes | 12 x 12 to 100 x 100 | JT, 304, 316, 316L | 26 Gauge (0.6mm) to 14 Gauge (2.0mm) | Mirror Finish & Matt Finish |
| Stainless Steel Rectangle Pipes | 10 x 20 to 50 x 150 | JT, 304, 316, 316L | 26 Gauge (0.6mm) to 14 Gauge (2.0mm) | Mirror Finish & Matt Finish |
| Stainless Steel Slotted Pipes |
40 x 40 x 15 50 x 50 x 15 60 x 40 x 15 |
JT, 304, 316, 316L | 26 Gauge (0.6mm) to 14 Gauge (2.0mm) | Mirror Finish & Matt Finish |
| Stainless Steel Oval Pipes |
19 x 45 13 x 33 |
JT, 304, 316, 316L | 26 Gauge (0.6mm) to 14 Gauge (2.0mm) | Mirror Finish & Matt Finish |
| OD mm | OD Inch | 0.50 mm (28G) |
0.60 mm (26G) |
0.70 mm (24G) |
0.80 mm (22G) |
0.90 mm (20G) |
1.20 mm (18G) |
1.45 mm (16G) |
1.96 mm (14G) |
|---|---|---|---|---|---|---|---|---|---|
| 10 | 3/8" | 0.720 | 0.850 | 0.980 | 1.110 | 1.240 | 1.600 | - | - |
| 12.7 10*10 |
1/2" | 0.920 | 1.100 | 1.300 | 1.440 | 1.600 | 2.100 | 2.500 | - |
| 15.875 12*12 |
5/8" | 1.160 | 1.400 | 1.600 | 1.820 | 2.000 | 2.700 | 3.200 | - |
| 19.05 15*15 10*20 25*12 Oval |
3/4" | 1.400 | 1.700 | 1.940 | 2.200 | 2.500 | 3.300 | 3.900 | 5.100 |
| 22 | 7/8" | 1.630 | 1.940 | 2.250 | 2.560 | 2.900 | 3.800 | 4.600 | 6.000 |
| 25.4 20*20 25*12 33*13 Oval |
1" | 1.900 | 2.250 | 2.600 | 3.000 | 3.400 | 4.400 | 5.300 | 7.000 |
| 31.75 25*25 10*40 |
1.25" | 2.360 | 2.800 | 3.300 | 3.740 | 4.200 | 5.600 | 6.700 | 8.900 |
| 35 19*45 Oval |
- | 2.600 | 3.100 | 3.600 | 4.140 | 4.700 | 6.200 | 7.400 | 9.800 |
| 38.1 20*40 30*30 24*36 10*50 |
1.5" | 2.840 | 3.400 | 3.960 | 4.500 | 5.100 | 6.800 | 8.100 | 10.800 |
| 48.26 25*50 |
1.5 NB | 3.610 | 4.300 | 5.000 | 5.740 | 6.500 | 8.600 | 10.400 | 13.800 |
| 50.8 40*40 |
2" | 3.800 | 4.600 | 5.300 | 6.100 | 6.800 | 9.100 | 10.900 | 14.500 |
| 63.5 50*50 25*75 35*65 40*60 |
2.5" | 4.760 | 5.700 | 6.650 | 7.600 | 8.500 | 11.400 | 13.700 | 18.330 |
| 76.2 40*80 60*60 |
3" | 5.720 | 6.900 | 8.000 | 9.120 | 10.300 | 13.700 | 16.600 | 22.100 |
| 101.6 80*80 50*100 |
4" | 7.640 | 9.200 | 10.700 | 12.200 | 13.700 | 18.400 | 22.200 | 29.700 |
| JSL GRADES | %C (min~max) |
%Mn (min~max) |
%P (min~max) |
%S (min~max) |
%SI (min~max) |
%CR (min~max) |
%NI (min~max) |
%MO (min~max) |
NPM (max) |
|---|---|---|---|---|---|---|---|---|---|
| J-201 | 0.15 | 5.5–7.5 | 0.06 | 0.03 | 1 | 16.00–18.00 | 3.50–5.50 | – | 2500 |
| J-202 | 0.15 | 7.5–10.0 | 0.06 | 0.03 | 1 | 17.00–19.00 | 4.00–6.00 | – | 2500 |
| JT | 0.10 | 9.0–10.0 | 0.01 | 0.01 | 0.75 | 14.5–16.5 | 0.25–0.35 | – | – |
| J4 | 0.10 | 8.50–10.0 | 0.08 | 0.01 | 0.75 | 15.00–16.00 | 1.00–2.00 | – | 2000 |
| JSL U DD | 0.15 (max) | 9.7–10.7 | 0.10 (max) | 0.03 (max) | 0.75 (max) | 15.1–16.0 | 0.45–0.60 | – | – |
| JSL U SD | 0.15 (max) | 9.7–10.30 | 0.10 (max) | 0.03 (max) | 0.75 (max) | 13.25–14.25 | 0.40–0.50 | – | – |
| J-301 | 0.15 | 2 | 0.045 | 0.03 | 1 | 16.00–18.00 | 6.00–8.00 | – | 1000 |
| J-304 | 0.07 | 2 | 0.045 | 0.03 | 0.75 | 17.50–19.50 | 8.00–10.50 | – | 1000 |
| J-304L | 0.03 | 2 | 0.045 | 0.03 | 0.75 | 17.50–19.50 | 8.00–12.00 | – | 1000 |
| J-316 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 16.00–18.00 | 10.00–14.00 | 2.00–3.00 | 1000 |
| J-316L | 0.03 | 2 | 0.045 | 0.03 | 0.75 | 16.00–18.00 | 10.00–14.00 | 2.00–3.00 | 1000 |
| J-410 | 0.08–0.15 | 1 | 0.04 | 0.03 | 1 | 11.50–13.50 | 0.75 max | – | – |
| J-420 | 0.15 min | 1 | 0.04 | 0.03 | 1 | 12.00–14.00 | 0.75 max | 0.50 max | – |
| J-409L | 0.03 | 1 | 0.04 | 0.02 | 1 | 10.50–11.70 | 0.50 max | – | 300 |
| JSL GRADES | Tensile Strength (MPA) Min. | % Yield Strength (MPA) Min. | % Elongation (min.) | Hardness (HRB) Max. |
|---|---|---|---|---|
| J-201 | 655 | 310 | 40 | 100 |
| J-202 | 620 | 260 | 40 | 100 |
| JT | 700 | 350 | 40 | 100 |
| J4 | 650 | 325 | 40 | 100 |
| JSL U DD | 700 | 350 | 40 | 100 |
| JSL U SD | 700 | 350 | 40 | 100 |
| J-301 | 515 | 205 | 40 | 95 |
| J-304 | 515 | 205 | 40 | 92 |
| J-304L | 485 | 170 | 40 | 92 |
| J-316 | 515 | 205 | 40 | 95 |
| J-316L | 485 | 170 | 40 | 95 |
| J-410 | 450 | 205 | 20 | 96 |
| J-420 | 690 | - | 15 | 96 |
| J-409L | 380 | 170 | 20 | 88 |
| J-409 Ni | 415 | 275 | 20 | 92 |
| SURFACE FINISH | DEFINITION | APPLICATIONS |
|---|---|---|
| No. 1 | Hot Rolled Annealed, Shot Blasted and Pickled | Pipes, Tubing, Chemical Tank, General Fabrication |
| No. 2 | Dull Cold Rolled Annealed and Pickled | Deep Drawn Utensils, Heat Exchanger, Exhaust Pipe |
| No. 2 B | Cold Rolled Annealed and Pickled and Skin Passed, Given an Appropriate Luster by Again Cold Rolling | Food Industry, Kitchen Utensils, Electric Equipment, Construction Material |
| BA | Bright Annealed Finish, Processed with Bright Heat Treatment After Cold Rolling | Decorative Usage, Kitchen Utensils, Electric Equipment, Building Construction |
| No. 3 | Cold Rolled Annealed and Pickled and Polished with 100 to 120 Grit. | Kitchen Utensils, Building Construction, Medical Equipment |
| No. 4 | Cold Rolled Annealed and Pickled and Polished with 150 to 180 Grit. | Kitchen Utensils, Building Construction, Medical Equipment |
| Scotch Brite | Very Fine Hairline Finish Generated by Polishing with Rolls Made out of Scotch Brite Material. | Architectural Purposes, Railway Cabins, Elevators Interiors, Paneling, Kitchen Appliances |